Rogers Corporation Poron® 4701-41-30 Urethane Foam, Soft, Enhanced Sealability

Category Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane Foam, Unreinforced
Manufacturer Rogers Corporation
Trade Name Poron®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation Poron® 4701-41-30 Urethane Foam, Soft, Enhanced Sealability.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Soft, enhanced sealability material offering greater closed-cell content for demanding vacuum sealing applications or low closure-force requirements.  Standard available thickness range from 0.031" to 0.500" (0.79 mm to 12.7 mm).Features and Benefits of PORON Products: Excellent compression set resistance which enables durable, long-term performance for gasketing, sealing, and cushioning.Low-outgassing and non-fogging, containing no plasticizers or residual chemicals to contaminate the device. The material will not become brittle and crumble and is non-corrosive to metal.Inherently flame retardant without the use of additives. Many of the materials meet flammability requirements of UL HBF and MVSS 302.Engineered urethane formulations offering a wide modulus range - 2-90 psi @ 25% deflection – for more design versatility requirements.Good chemical resistanceEasy to fabricate, die-cuts cleanly and works with a broad range of adhesivesBroad range of formulas and thicknesses from 0.012" to 0.500" (0.43mm to 12.7mm)Applications:
Physical Properties Metric English Comments
Density 0.481 g/cc
0.0174 lb/in³
ASTM D3574-95 Test A
Water Absorption 6.0 %
6.0 %
Immersion; ASTM D570-95
Moisture Absorption at Equilibrium 2.0 %
2.0 %
High Humidity; AMS 3568-95
Thickness 787 - 1140 microns
31.0 - 45.0 mil
Range of Thicknesses Available
Outgassing - Total Mass Loss 0.060 %

@Temperature 125 °C,
Time 86400 sec
0.060 %

@Temperature 257 °F,
Time 24.0 hour
CVCM; at 7000 Pa; ASTM E595-93
0.65 %

@Temperature 125 °C,
Time 86400 sec
0.65 %

@Temperature 257 °F,
Time 24.0 hour
WVR; at 7000 Pa; ASTM E595-93
1.0 %

@Temperature 125 °C,
Time 86400 sec
1.0 %

@Temperature 257 °F,
Time 24.0 hour
TML; at 7000 Pa; ASTM E595-93
Mechanical Properties Metric English Comments
Hardness, Shore O 55
55
ASTM D2240-97
Tensile Strength >= 0.827 MPa
>= 120 psi
ASTM D3574-75 Test E
1.03 MPa
149 psi
Typical; ASTM D3574-75 Test E
Elongation at Break >= 100 %
>= 100 %
ASTM D3574-75 Test E
136 %
136 %
Typical; ASTM D3574-75 Test E
Compressive Yield Strength 0.103 - 0.276 MPa

@Strain 25.0 %
15.0 - 40.0 psi

@Strain 25.0 %
Range, 0.2"/min. strain rate
0.193 MPa

@Strain 25.0 %
28.0 psi

@Strain 25.0 %
Typical value, 0.2"/min. strain rate
Tear Strength >= 2.60 kN/m
>= 14.8 pli
ASTM D264-91 Die C
3.20 kN/m
18.3 pli
Typical; ASTM D264-91 Die C
Compression Set 5.0 %

@Temperature 23.0 °C
5.0 %

@Temperature 73.4 °F
ASTM D1667-90 Test D
5.0 %

@Temperature 121 °C
5.0 %

@Temperature 250 °F
autoclaved 5 hrs; ASTM D3574-95 J/Test D
10 %

@Temperature 70.0 °C
10 %

@Temperature 158 °F
ASTM D3574-95 Test D
Thermal Properties Metric English Comments
CTE, linear 230 - 310 µm/m-°C
128 - 172 µin/in-°F
Maximum Service Temperature, Air 90.0 °C
194 °F
Constant use; SAE J-2236
121 °C
250 °F
Intermittent use; ASTM D746-98
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257-99
Dielectric Constant 1.71

@Time 86400 sec
1.71

@Time 24.0 hour
50% RH; ASTM D150
Dielectric Strength 1.97 kV/mm
50.0 kV/in
ASTM D149-97a
Dissipation Factor 0.050
0.050
ASTM D150-98