RheTech Products FRG130-01 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Flame Retardant, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FRG130-01 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Flame Retardant, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Electrical component housingsSunroof componentsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 30 % | 30 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0012 cm/cm | 0.0012 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 76 | 76 | ASTM D2240 |
| Tensile Strength at Break | 73.8 MPa | 10700 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 5.65 GPa | 820 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.339 J | 0.250 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 159 °C | 318 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 290 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 191 - 199 °C | 375 - 390 °F | |
| Middle Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Front Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |
| Mold Temperature | 23.9 - 35.0 °C | 75.0 - 95.0 °F | |
| Drying Temperature | 51.7 - 65.6 °C | 125 - 150 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 8.27 MPa | 400 - 1200 psi | |
| Hold Pressure | 2.07 - 6.89 MPa | 300 - 1000 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi |
Users viewing this material also viewed the following:
- Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet
- SABIC Innovative Plastics LNP THERMOCOMP EXTC8141 PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM3020 PPE+PS
- Samsung Cheil Industries Infino® TP-1020 PC, Unreinforced Transparent
- A. Schulman POLYBATCH™ Blue 4021 Concentrate Based in Polyethylene
- A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin
- DSM Stanyl® TW271F6 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Dry)
- EMS-Grivory Grivory® F 47 NL nat 6028 PA6
- Amity Thermosets ATG 115 Phenolic Molding Organic Filler, Compression Molded
- 3M Controltac™ IJ180-10 Graphic Film
Copyright © lookpolymers.com All Rights Reserved