Resinlab® EP1285HD-12 Highly Filled, Medium Viscosity Casting Resin

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin , Epoxy, Cast, Metal Filled
Manufacturer Resinlab®
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinlab® EP1285HD-12 Highly Filled, Medium Viscosity Casting Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low CTE combined with a moderate free flowing viscosity. They give excellent resistance to acids, bases, water, and most organic compounds. The high filler content also enhances resistance to thermal cycle stresses. The choice of hardener allows the user to choose a variety of reactivity’s, viscosities, thermal ranges and environmental resistance capabilities. The resin contains a high loading of abrasive aluminum oxide filler, which can introduce wear considerations for wetted components of meter-mix and dispensing equipment. Warming the assembly prior to filling will aid in flow and air release. Additional vacuum degassing may be desired for some applications.Information Provided by Resinlab L.L.C., an Ellsworth Adhesives Company.
Physical Properties Metric English Comments
Specific Gravity 2.15 g/cc
2.15 g/cc
Water Absorption 0.030 %

@Time 86400 sec
0.030 %

@Time 24.0 hour
TM R050-35
Viscosity 20000 cP
20000 cP
Mixed, RVT, #6, 2.5 rpm; TM R050-12
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
Mechanical Properties Metric English Comments
Hardness, Shore D 95
95
TM R050-19
Tensile Strength at Break 17.2 MPa
2500 psi
TM R050-36
Tensile Strength, Ultimate 17.2 MPa
2500 psi
TM R050-36
Tensile Strength, Yield 6.89 MPa
1000 psi
TM R050-36
Elongation at Break 0.00 - 1.0 %
0.00 - 1.0 %
TM R050-36
Tensile Modulus 7.58 GPa
1100 ksi
TM R050-36
Compressive Yield Strength 62.1 MPa
9000 psi
TM R050-38
Compressive Strength 68.9 MPa
10000 psi
Break; TM R050-38
86.2 MPa
12500 psi
Ultimate; TM R050-38
Compressive Modulus 4.48 GPa
650 ksi
TM R050-38
Adhesive Bond Strength 11.7 MPa
1700 psi
Lap shear; 2024 T3 Al Abraded / MEK Wipe
Thermal Properties Metric English Comments
CTE, linear 31.0 µm/m-°C

@Temperature <=132 °C
17.2 µin/in-°F

@Temperature <=270 °F
below Tg
98.0 µm/m-°C

@Temperature >=132 °C
54.4 µin/in-°F

@Temperature >=270 °F
above Tg
Thermal Conductivity 1.28 W/m-K
8.88 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 150 °C
302 °F
Minimum Service Temperature, Air -50.0 °C
-58.0 °F
Glass Transition Temp, Tg 132 °C
270 °F
TM R050-25
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Dielectric Constant 5.4
5.4
Dielectric Strength 15.0 kV/mm
380 kV/in
Processing Properties Metric English Comments
Cure Time 30.0 - 60.0 min

@Temperature 120 °C
0.500 - 1.00 hour

@Temperature 248 °F
120 - 240 min

@Temperature 100 °C
2.00 - 4.00 hour

@Temperature 212 °F
480 - 720 min

@Temperature 80.0 °C
8.00 - 12.0 hour

@Temperature 176 °F
Pot Life 180 - 240 min
180 - 240 min
Mass: 100g; TM R050-17
Descriptive Properties Value Comments
Color Black
Mix Ratio 15.55:1
Weight
6.55:1
Volume