Reliance Industries Reclair O19010 Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded
Manufacturer Reliance Industries
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Reliance Industries Reclair O19010 Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Blow film Linear Low Density Polyethylene grade. Reclair O19010 is octene comonomer based, with optimum levels of antioxidants, antiblocking agents, slip additives, and polymer processing aids. This grade is good for heavy duty applications and liquid packaging. Characteristics:excellent seal through contamination, excellent toughness, excellent impact strength, and excellent tear resistance. Information provided by Reliance Industries
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D1505
Melt Flow 0.90 g/10 min

@Load 2.16 kg
0.90 g/10 min

@Load 4.76 lb
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 12.5 MPa
1810 psi
ASTM D882
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM D882
Film Elongation at Break, MD 650 %
650 %
ASTM D882
Film Elongation at Break, TD 800 %
800 %
ASTM D882
Coefficient of Friction, Dynamic 0.12
0.12
ASTM D1894
Coefficient of Friction, Static 0.20
0.20
ASTM D1894
Elmendorf Tear Strength, MD 13.8 g/micron
351 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 27.6 g/micron
701 g/mil
ASTM D1922
Dart Drop 7.00 g/micron
178 g/mil
F<sub>50</sub>,38mm dart 66mm height; ASTM D1709
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ASTM D882
Film Tensile Strength at Break, TD 35.0 MPa
5080 psi
ASTM D882
Optical Properties Metric English Comments
Gloss 80 %
80 %
60; ASTM D523