Reliance Industries PVAXX H60

Category Polymer , Renewable/Recycled Polymer , Thermoplastic
Manufacturer Reliance Industries
Trade Name PVAXX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Reliance Industries PVAXX H60.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The key property of all PVAXX polymer is this product`s unique capacity to biodegrade into non-toxic residues under both aerobic and non-aerobic conditions.Information provided by Reliance Industries
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
ASTM D792
Melt Flow 10.5 g/10 min

@Load 2.16 kg,
Temperature 210 °C
10.5 g/10 min

@Load 4.76 lb,
Temperature 410 °F
Mechanical Properties Metric English Comments
Hardness, Rockwell R 98
98
ASTM D 785
Tensile Strength, Ultimate 11.5 MPa
1670 psi
ASTM D638
Tensile Strength, Yield 28.7 MPa
4160 psi
ASTM D368
Tensile Modulus 0.383 GPa
55.6 ksi
ASTM D638
Flexural Strength 20.2 MPa
2930 psi
2mm Deflection; ASTM D790
43.0 MPa
6240 psi
ASTM D790
Flexural Modulus 2.18 GPa
316 ksi
ASTM D790
Izod Impact, Notched (ISO) 0.510 kJ/m²
0.243 ft-lb/in²
ASTM D256
Izod Impact, Unnotched (ISO) 4.33 kJ/m²
2.06 ft-lb/in²
ASTM D256
Charpy Impact Unnotched 0.306 J/cm²
1.46 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Melting Point 213 °C
415 °F
DSC Peak
Deflection Temperature at 1.8 MPa (264 psi) 69.0 - 75.0 °C
156 - 167 °F
ASTM D648
Vicat Softening Point 184 °C
363 °F
ASTM D1525
Oxygen Index 18 %
18 %
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+11 ohm-cm
3.00e+11 ohm-cm
Surface Resistance 2.00e+14 ohm
2.00e+14 ohm