Ravago Manufacturing Americas Hylex® P1010G10 HB Polycarbonate, 10% Fiberglass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1010G10 HB Polycarbonate, 10% Fiberglass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 0.14 % | 0.14 % | 24-Hr Immersion; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 5.0 - 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 9.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Yield | 13 % | 13 % | ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 3.448 GPa | 500.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 154 °C | 309 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm @Thickness 3.17 mm |
410 kV/in @Thickness 0.125 in |
in air; ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible C90A0 Polyvinyl Chloride, Flexible (PVC, Flexible)
- DuPont Performance Polymers Zytel® HTN 54G35HSLR NC010 Polyphthalamide (PPA) (Unverified Data**)
- ExxonMobil Exceed™ 1018CA Premium Blown Film Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1850/GF/30/TF/15/BK PBT, with glass fiber and PTFE
- SABIC Innovative Plastics LNP STAT-KON DE0021E PC
- American Elements Lutetium Nanoparticles
- Covestro Apec® HT KU 1-9357/2 High-Heat Polycarbonate, 20% Glass Fiber
- Arlon 41940C020 0.015" Uncured, Unsupported Silicone Rubber on Release Carrier
- ExxonMobil Santoprene® 211-64 Thermoplastic Elastomer (discontinued **)