- Acrylonitrile Butadiene Styrene (ABS), Molded
- Ravago Manufacturing Americas Hylac® HF143 ABS
Ravago Manufacturing Americas Hylac® HF143 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylac® HF143 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 4.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 14 g/10 min @Load 3.80 kg, Temperature 230 °C |
14 g/10 min @Load 8.38 lb, Temperature 446 °F |
Cond I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Tensile Modulus | 2.79 GPa | 405 ksi | ASTM D638 |
| Flexural Yield Strength | 74.5 MPa | 10800 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 1.49 J/cm | 2.80 ft-lb/in | 0.25 in; ASTM D256 |
| 1.71 J/cm | 3.20 ft-lb/in | 73°F, 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 97.2 µm/m-°C @Temperature -40.0 - 176 °C |
54.0 µin/in-°F @Temperature -40.0 - 349 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.9 °C | 192 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 105 °C | 221 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 179 - 199 °C | 355 - 390 °F | |
| Middle Barrel Temperature | 199 - 221 °C | 390 - 430 °F | |
| Front Barrel Temperature | 216 - 235 °C | 420 - 455 °F | |
| Nozzle Temperature | 210 - 229 °C | 410 - 445 °F | |
| Melt Temperature | 241 °C | 465 °F | |
| Mold Temperature | 48.9 - 60.0 °C | 120 - 140 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % | |
| Injection Pressure | 5.86 - 6.89 MPa | 850 - 1000 psi | |
| Back Pressure | 0.483 - 0.965 MPa | 70.0 - 140 psi | |
| Shot Size | 40 - 80 % | 40 - 80 % | |
| Screw Speed | 50 - 90 rpm | 50 - 90 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 710 to 850 psi | |
| Injection Rate | Slow-Moderate |