Radici Raditer® B RV 100 Polybutylene Terephthalate with 10% Glass fiber

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
Manufacturer	Radici Group Plastics
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Radici Raditer® B RV 100 Polybutylene Terephthalate with 10% Glass fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Raditer® B RV 100 is a glass fiber reinforced thermoplastic polyester based on polybutylene terephthalate. The PBT compounds combine excellent thermal, mechanical, electrical and chemical properties with very good dimensional stability.Suggestions for application: Technical items with a wide range of stiffness.Information provided by Radici group.

Physical Properties	Metric	English	Comments
Specific Gravity	1.36 g/cc	1.36 g/cc	ISO 1183
Moisture Absorption at Equilibrium	0.18 %	0.18 %	ISO 62

Mechanical Properties	Metric	English	Comments
Elongation at Break	75 %	75 %	ISO 527-2/1A
Tensile Modulus	4.40 GPa	638 ksi	ISO 527-2/1A
Flexural Strength	125 MPa	18100 psi	ISO 178/1A
Flexural Modulus	3.60 GPa	522 ksi	ISO 178/1A
Charpy Impact Unnotched	3.00 J/cm²	14.3 ft-lb/in²	ISO 179 eU
Charpy Impact, Notched	0.450 J/cm²	2.14 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	225 °C	437 °F	ISO 11357-1-3
Deflection Temperature at 0.46 MPa (66 psi)	220 °C	428 °F	ISO 75-2/Af
Deflection Temperature at 1.8 MPa (264 psi)	185 °C	365 °F	ISO 75-2/Af
Vicat Softening Point	200 °C @Load 5.10 kg	392 °F @Load 11.2 lb	50°C/h; ISO 306/B50
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in
Glow Wire Test	700 °C @Thickness 2.00 mm	1290 °F @Thickness 0.0787 in	CEI 695-2-1/2