Radici Raditer® B N 100 T Polybutylene Terephthalate

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer	Radici Group Plastics
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Radici Raditer® B N 100 T Polybutylene Terephthalate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Raditer® B N 100T is a high impact modified thermoplastic polyester based on polybutylene terephthalate. The PBT compounds combine excellent thermal, mechanical, electrical and chemical properties with very good dimensional stability.Suggestions for application: Technical items that require good impact strength, stiffness and low warpage.Information provided by Radici group.

Physical Properties	Metric	English	Comments
Specific Gravity	1.28 g/cc	1.28 g/cc	ISO 1183
Moisture Absorption at Equilibrium	0.18 %	0.18 %	ISO 62

Mechanical Properties	Metric	English	Comments
Elongation at Break	40 %	40 %	ISO 527-2/1A
Tensile Modulus	2.00 GPa	290 ksi	ISO 527-2/1A
Flexural Strength	65.0 MPa	9430 psi	ISO 178/1A
Flexural Modulus	1.90 GPa	276 ksi	ISO 178/1A
Charpy Impact Unnotched	NB	NB	ISO 179 eU
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	225 °C	437 °F	ISO 11357-1-3
Deflection Temperature at 0.46 MPa (66 psi)	160 °C	320 °F	ISO 75-2/Af
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F	ISO 75-2/Af
Vicat Softening Point	65.0 °C @Load 5.10 kg	149 °F @Load 11.2 lb	50°C/h; ISO 306/B50
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in
Glow Wire Test	650 °C @Thickness 2.00 mm	1200 °F @Thickness 0.0787 in	CEI 695-2-1/2