Radici Radilon® CS 35FL (dry) Nylon 6/66

Category Polymer , Thermoplastic , Nylon , Nylon 6/66
Manufacturer Radici Group Plastics
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Radici Radilon® CS 35FL (dry) Nylon 6/66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Radilon® CS is a range of polyamide 6/66 copolymers obtained through the polymerization of caprolactam and hexamethylendiamine salt with adipic acid.Information provided by Radici group.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
Water Absorption 10.2 %
10.2 %
Moisture Absorption at Equilibrium 3.0 %
3.0 %
Viscosity Measurement 205
205
cm³/g Viscosity Number
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
Elongation at Break >= 50 %
>= 50 %
Nominal
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 3.40 GPa
493 ksi
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Charpy Impact, Notched 0.580 J/cm²

@Temperature -30.0 °C
2.76 ft-lb/in²

@Temperature -22.0 °F
0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 210 °C
410 °F
Deflection Temperature at 0.46 MPa (66 psi) 70.0 °C
158 °F
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Vicat Softening Point 70.0 °C

@Load 5.10 kg
158 °F

@Load 11.2 lb
50°C/h
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+11 ohm-cm
>= 1.00e+11 ohm-cm