RTP Company RTP 900 TFE 5 Polysulfone (PSU), PTFE Lubricated

Category Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone with PTFE/Silicone Filler
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 900 TFE 5 Polysulfone (PSU), PTFE Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D 792
Filler Content 5 %
5 %
Primary Additive
Linear Mold Shrinkage 0.0080 cm/cm

@Thickness 3.17 mm
0.0080 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.5 MPa
9500 psi
ASTM D 638
Elongation at Break 7.0 - 12 %
7.0 - 12 %
ASTM D 638
Tensile Modulus 2.55 GPa
370 ksi
ASTM D 638
Flexural Strength 110 MPa
16000 psi
ASTM D 790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D 790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.17 mm
1.20 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 16.0 J/cm

@Thickness 3.17 mm
30.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 174 °C
345 °F
ASTM D 648
Flammability, UL94 V-1

@Thickness 1.59 mm
V-1

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 332 - 371 °C
630 - 700 °F
Mold Temperature 93.3 - 149 °C
200 - 300 °F
Drying Temperature 135 °C
275 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi