RTP Company RTP 705 High Density Polyethylene (HDPE), Glass Fiber
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | RTP Company |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 705 High Density Polyethylene (HDPE), Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D 792 |
| Filler Content | 30 % | 30 % | Primary Additive |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0010 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D 638 |
| Elongation at Break | 2.0 - 4.0 % | 2.0 - 4.0 % | ASTM D 638 |
| Tensile Modulus | 5.86 GPa | 850 ksi | ASTM D 638 |
| Flexural Strength | 73.8 MPa | 10700 psi | ASTM D 790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
D 256 |
| Izod Impact, Unnotched | 3.47 J/cm @Thickness 3.17 mm |
6.50 ft-lb/in @Thickness 0.125 in |
ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 232 °C | 380 - 450 °F | |
| Mold Temperature | 21.1 - 65.6 °C | 70.0 - 150 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 hour | 2 hour | |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi |
Users viewing this material also viewed the following:
- Nylene® PA6 Glass/Mineral Filled 7115 HS Nylon 6
- Kraiburg TPE THERMOLAST® K TF5EFD Elastic Film TPE
- Momentive Performance Materials HV 6/600 Heat Cured Rubber - STEAM Resistant
- SABIC Innovative Plastics Valox® ENH3500 PBT (Europe-Africa-Middle East)
- Styrolution Terluran® EHI-4 NR ABS Extrusion Application
- A. Schulman POLYBATCH™ Bright While LL80250 Concentrate Based In LLDPE
- Zhejiang Juner PA-A6-4 Non-Reinforced
- ExxonMobil 2 Mobilux EP
- DSM Arnite® TB6 260 PBT-GB30
- Samyang Trimma® SD6350T PMMA, Opaque
Copyright © lookpolymers.com All Rights Reserved