RTP Company RTP 700 SI 2 High Density Polyethylene (HDPE), Silicone Lubricated

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 700 SI 2 High Density Polyethylene (HDPE), Silicone Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 0.940 g/cc
0.940 g/cc
ASTM D 792
Filler Content 2 %
2 %
Primary Additive
Linear Mold Shrinkage 0.013 - 0.028 cm/cm

@Thickness 3.17 mm
0.013 - 0.028 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 19.3 MPa
2800 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 1.10 GPa
160 ksi
ASTM D 638
Flexural Strength 20.7 MPa
3000 psi
ASTM D 790
Flexural Modulus 0.896 GPa
130 ksi
ASTM D 790
Izod Impact, Notched 0.908 J/cm

@Thickness 3.17 mm
1.70 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 10.7 J/cm

@Thickness 3.17 mm
20.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 48.9 °C
120 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 193 - 232 °C
380 - 450 °F
Mold Temperature 21.1 - 65.6 °C
70.0 - 150 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 2 hour
2 hour
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi