RTP Company RTP 700 AR 15 TFE 15 High Density Polyethylene (HDPE), Aramid Fiber Reinforced - PTFE Lubricated
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | RTP Company |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 700 AR 15 TFE 15 High Density Polyethylene (HDPE), Aramid Fiber Reinforced - PTFE Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D 792 |
| Filler Content | 15 % | 15 % | Primary Additive |
| Linear Mold Shrinkage | 0.012 cm/cm @Thickness 3.17 mm |
0.012 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 26.2 MPa | 3800 psi | ASTM D 638 |
| Elongation at Break | 8.0 - 12 % | 8.0 - 12 % | ASTM D 638 |
| Tensile Modulus | 1.59 GPa | 230 ksi | ASTM D 638 |
| Flexural Strength | 37.9 MPa | 5500 psi | ASTM D 790 |
| Flexural Modulus | 1.59 GPa | 230 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm |
1.50 ft-lb/in @Thickness 0.125 in |
D 256 |
| Izod Impact, Unnotched | 3.74 J/cm @Thickness 3.17 mm |
7.00 ft-lb/in @Thickness 0.125 in |
ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D 648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 232 °C | 380 - 450 °F | |
| Mold Temperature | 21.1 - 65.6 °C | 70.0 - 150 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 hour | 2 hour | |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi |
Users viewing this material also viewed the following:
- Eastman Tenite 371A-08 Cellulose Acetate Propionate (discontinued **)
- Kraiburg TPE Hipex® HX8IMN Thermoplastic Elastomer, High Performance
- Lubrizol ESTANE® GP85AB Ester Based Thermoplastic Polyurethane
- Constellium PLAN 5083 Aluminum Rolled Plate
- Dow Saran® F-239 PVDC
- DuPont Teijin Films Teijin® Tetoron® HS Polyester Film, 400 Gauge
- BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Dry)
- 3M Scotch-Weld™ DP100 Plus Clear Epoxy Adhesive
- Solvay RHODOLINE® HP Surfactant
Copyright © lookpolymers.com All Rights Reserved