RTP Company RTP 6003-45A Z Specialty Thermoplastic Elastomer, Bondable to PC/PMMA, PC/PBT

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 6003-45A Z Specialty Thermoplastic Elastomer, Bondable to PC/PMMA, PC/PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 0.980 g/cc
0.980 g/cc
ASTM D 792
Linear Mold Shrinkage 0.030 - 0.060 cm/cm

@Thickness 3.17 mm
 0.030 - 0.060 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore A 44
44
10 s delay; ASTM D 2240
Tensile Strength at Break 6.89 MPa

@Thickness 3.17 mm
 1000 psi

@Thickness 0.125 in
 Die C; 20 in/min (500 mm/min); ASTM D412
Elongation at Break 1100 %

@Thickness 3.17 mm
 1100 %

@Thickness 0.125 in
 Die C; 20 in/min (500 mm/min); ASTM D412
Tear Strength 24.5 kN/m
140 pli
Die C; ASTM D 624
Peel Strength 3.51 kN/m
20.0 pli
PC/PBT; Failure Type D; 90 degrees, 20 in/min (500 mm/min); ISO 813
4.21 kN/m
24.0 pli
PC/PMMA; Failure Type D; 90 degrees, 20 in/min (500 mm/min); ISO 813
Compression Set 16 %

@Temperature 23.0 °C,
Time 79200 sec
 16 %

@Temperature 73.4 °F,
Time 22.0 hour
 Method B; Type 2; ASTM D 395
66 %

@Temperature 70.0 °C,
Time 79200 sec
 66 %

@Temperature 158 °F,
Time 22.0 hour
 Method B; Type 2; ASTM D 395
Processing Properties Metric English Comments
Melt Temperature 193 - 238 °C
380 - 460 °F
Mold Temperature 21.1 - 48.9 °C
70.0 - 120 °F
Drying Temperature 76.7 °C
170 °F
Dry Time 2 - 4 hour
2 - 4 hour
Moisture Content <= 0.040 %
<= 0.040 %
Injection Pressure 34.5 - 103 MPa
5000 - 15000 psi