RTP Company RTP 6003-45A MD NATURAL Specialty Thermoplastic Elastomer; ISO 10993 Tested

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 6003-45A MD NATURAL Specialty Thermoplastic Elastomer; ISO 10993 Tested.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 0.980 g/cc
0.980 g/cc
ASTM D 792
Linear Mold Shrinkage 0.030 - 0.060 cm/cm

@Thickness 3.20 mm
 0.030 - 0.060 in/in

@Thickness 0.126 in
 ASTM D 955
Mechanical Properties Metric English Comments
Hardness, Shore A 44

@Time 10.0 sec
 44

@Time 0.00278 hour
 ASTM D 2240
Tensile Strength at Break 6.89 MPa

@Thickness 3.20 mm
 1000 psi

@Thickness 0.126 in
 Break; Die C; 20 in/min (500 mm/min); ASTM D 412
Elongation at Break 1100 %

@Thickness 3.20 mm
 1100 %

@Thickness 0.126 in
 Die C, 20 in/min (500 mm/min); ASTM D 412
Tear Strength 24.5 kN/m
140 pli
Die C; ASTM D 624
Peel Strength 3.51 kN/m
20.0 pli
90 degrees, 20 in/min (500 mm/min); vs. PC/PBT; Failure Type D; ISO 813
4.21 kN/m
24.0 pli
90 degrees, 20 in/min (500 mm/min); vs. PC/PMMA; Failure Type D; ISO 813
Compression Set 16 %

@Temperature 23.0 °C,
Time 79200 sec
 16 %

@Temperature 73.4 °F,
Time 22.0 hour
 Method B; Type 2; ASTM D 395
66 %

@Temperature 70.0 °C,
Time 79200 sec
 66 %

@Temperature 158 °F,
Time 22.0 hour
 Method B; Type 2; ASTM D 395
Processing Properties Metric English Comments
Melt Temperature 193 - 238 °C
380 - 460 °F
Mold Temperature 21.1 - 48.9 °C
70.0 - 120 °F
Drying Temperature 76.7 °C

@Time 7200 - 14400 sec
 170 °F

@Time 2.00 - 4.00 hour
Moisture Content <= 0.040 %
<= 0.040 %