RTP Company RTP 600 HB Acrylonitrile Butadiene Styrene (ABS), UL94 HB

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 600 HB Acrylonitrile Butadiene Styrene (ABS), UL94 HB.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D 792
Water Absorption 0.30 %
0.30 %
24 hrs @ 23°C; ASTM D 570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm

@Thickness 3.17 mm
0.0040 - 0.0060 in/in

@Thickness 0.125 in
ASTM D955
Melt Flow 4.0 - 5.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
4.0 - 5.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.7 MPa
6200 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 2.41 GPa
350 ksi
ASTM D 638
Flexural Strength 68.9 MPa
10000 psi
ASTM D 790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D 790
Izod Impact, Notched 2.94 J/cm

@Thickness 3.17 mm
5.50 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 10.7 J/cm

@Thickness 3.17 mm
20.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 102 °C
215 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 98.9 °C
210 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 204 - 238 °C
400 - 460 °F
Mold Temperature 62.8 - 85.0 °C
145 - 185 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 2 hour
2 hour
Moisture Content 0.10 %
0.10 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi