RTP Company RTP 4799 X 117571 E Polytrimethylene Terephthalate (PTT) Glass Fiber - Flame Retardant - Halogen Free

Category Polymer , Thermoplastic , Polyester, TP , Polytrimethylene Terephthalate (PTT)
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 4799 X 117571 E Polytrimethylene Terephthalate (PTT) Glass Fiber - Flame Retardant - Halogen Free.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.49 g/cc
1.49 g/cc
ASTM D 792
Additive Loading 20 %
20 %
Primary Additive
Linear Mold Shrinkage 0.0022 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0022 - 0.0040 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 93.1 MPa
13500 psi
ASTM D 638
Elongation at Break 1.5 - 2.5 %
1.5 - 2.5 %
ASTM D 638
Tensile Modulus 9.38 GPa
1360 ksi
ASTM D 638
Flexural Strength 128 MPa
18500 psi
ASTM D 790
Flexural Modulus 8.62 GPa
1250 ksi
ASTM D 790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.20 mm
1.20 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 4.54 J/cm

@Thickness 3.20 mm
8.50 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Processing Properties Metric English Comments
Melt Temperature 232 - 260 °C
450 - 500 °F
Mold Temperature 87.8 - 121 °C
190 - 250 °F
Drying Temperature 127 °C

@Time 14400 - 21600 sec
260 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.010 %
0.010 %
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi