RTP Company RTP 4799 X 115376 C Polytrimethylene Terephthalate (PTT) Biobased Polyester - Glass Fiber - 26% Bio-Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polytrimethylene Terephthalate (PTT)
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 4799 X 115376 C Polytrimethylene Terephthalate (PTT) Biobased Polyester - Glass Fiber - 26% Bio-Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.57 g/cc
1.57 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0030 cm/cm

@Thickness 3.20 mm
0.0030 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 152 MPa
22000 psi
ASTM D 638
Elongation at Break 3.0 %
3.0 %
ASTM D 638
Flexural Strength 228 MPa
33000 psi
ASTM D 790
Flexural Modulus 9.65 GPa
1400 ksi
ASTM D 790
Izod Impact, Notched 0.747 J/cm

@Thickness 3.20 mm
1.40 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 5.87 J/cm

@Thickness 3.20 mm
11.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 224 °C
435 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 232 - 260 °C
450 - 500 °F
Mold Temperature 87.8 - 121 °C
190 - 250 °F
Drying Temperature 127 °C

@Time 14400 - 21600 sec
260 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.010 %
0.010 %
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi