RTP Company RTP 4405 TFE 15 High Temperature Nylon (HTN), Glass Fiber - PTFE Lubricated

Category Polymer , Thermoplastic , Nylon
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 4405 TFE 15 High Temperature Nylon (HTN), Glass Fiber - PTFE Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.55 g/cc
1.55 g/cc
ASTM D 792
Filler Content 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0040 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 148 MPa
21500 psi
ASTM D 638
Elongation at Break 1.5 - 2.5 %
1.5 - 2.5 %
ASTM D 638
Tensile Modulus 9.31 GPa
1350 ksi
ASTM D 638
Flexural Strength 200 MPa
29000 psi
ASTM D 790
Flexural Modulus 10.0 GPa
1450 ksi
ASTM D 790
Izod Impact, Notched 0.801 J/cm

@Thickness 3.17 mm
1.50 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 3.74 J/cm

@Thickness 3.17 mm
7.00 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 310 - 343 °C
590 - 650 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 4 hour
4 hour
Moisture Content 0.10 %
0.10 %
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi