RTP Company RTP 4085 TFE 13 SI 2 Polyphthalamide (PPA), Carbon Fiber - PTFE Lubricated - Silicone Lubricated

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Carbon Fiber + PTFE Filled
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 4085 TFE 13 SI 2 Polyphthalamide (PPA), Carbon Fiber - PTFE Lubricated - Silicone Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D 792
Filler Content 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.00050 - 0.0020 cm/cm

@Thickness 3.17 mm
0.00050 - 0.0020 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 248 MPa
36000 psi
ASTM D 638
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
ASTM D 638
Tensile Modulus 24.8 GPa
3600 ksi
ASTM D 638
Flexural Strength 352 MPa
51000 psi
ASTM D 790
Flexural Modulus 22.4 GPa
3250 ksi
ASTM D 790
Izod Impact, Notched 0.747 J/cm

@Thickness 3.17 mm
1.40 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 6.94 J/cm

@Thickness 3.17 mm
13.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity <= 1e+05
<= 1e+05
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 302 - 329 °C
575 - 625 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 107 °C
225 °F
Dry Time 4 - 6 hour
4 - 6 hour
Moisture Content 0.050 %
0.050 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi