RTP Company RTP 4011 A (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 4011 A (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.75 g/cc
1.75 g/cc
ASTM D 792
Filler Content 60 %
60 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0020 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
ASTM D 638
Tensile Modulus 20.7 GPa
3000 ksi
ASTM D 638
Flexural Strength 331 MPa
48000 psi
ASTM D 790
Flexural Modulus 20.7 GPa
3000 ksi
ASTM D 790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.17 mm
2.00 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 9.08 J/cm

@Thickness 3.17 mm
17.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Processing Properties Metric English Comments
Melt Temperature 329 - 343 °C
625 - 650 °F
Mold Temperature 65.6 - 163 °C
150 - 325 °F
Drying Temperature 107 °C
225 °F
Dry Time 4 - 6 hour
4 - 6 hour
Moisture Content 0.10 %
0.10 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi