RTP Company RTP 4009 Polyphthalamide (PPA), Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 4009 Polyphthalamide (PPA), Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.64 g/cc
1.64 g/cc
ASTM D 792
Filler Content 50 %
50 %
Primary Additive
Water Absorption 0.16 %
0.16 %
24 hrs @ 23°C; ASTM D 570
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 125
125
ASTM D 785
Tensile Strength at Break 248 MPa
36000 psi
ASTM D 638
Elongation at Break 2.0 - 3.0 %
2.0 - 3.0 %
ASTM D 638
Tensile Modulus 18.5 GPa
2680 ksi
ASTM D 638
Flexural Strength 365 MPa
53000 psi
ASTM D 790
Flexural Modulus 17.2 GPa
2500 ksi
ASTM D 790
Izod Impact, Notched 1.17 J/cm

@Thickness 3.17 mm
2.20 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 9.08 J/cm

@Thickness 3.17 mm
17.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 16.2 µm/m-°C
9.00 µin/in-°F
E 831
Deflection Temperature at 1.8 MPa (264 psi) 282 °C
540 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D 257
Dielectric Constant 6.1

@Frequency 1.00e+6 Hz
6.1

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Dielectric Strength 18.9 kV/mm
480 kV/in
Short Term; in oil; ASTM D 149
Dissipation Factor 0.0090

@Frequency 1.00e+6 Hz
0.0090

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Processing Properties Metric English Comments
Melt Temperature 302 - 329 °C
575 - 625 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 107 °C
225 °F
Dry Time 4 - 6 hour
4 - 6 hour
Moisture Content 0.050 %
0.050 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi