RTP Company RTP 4009 MS Polyphthalamide (PPA), Glass Fiber - Molybdenum Disulfide

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 4009 MS Polyphthalamide (PPA), Glass Fiber - Molybdenum Disulfide.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.64 g/cc
1.64 g/cc
ASTM D 792
Additive Loading 50 %
50 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0040 in/in

@Thickness 0.125 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 179 MPa
26000 psi
ASTM D 638
Elongation at Break 2.0 - 3.0 %
2.0 - 3.0 %
ASTM D 638
Tensile Modulus 15.9 GPa
2300 ksi
ASTM D 638
Flexural Strength 296 MPa
43000 psi
ASTM D 790
Flexural Modulus 15.5 GPa
2250 ksi
ASTM D 790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.17 mm
2.00 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Izod Impact, Unnotched 9.61 J/cm

@Thickness 3.17 mm
18.0 ft-lb/in

@Thickness 0.125 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 249 °C
480 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 302 - 329 °C
575 - 625 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 107 °C

@Time 14400 - 21600 sec
225 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.050 %
0.050 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi