RTP Company RTP 4008 A FR (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber - Flame Retardant

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 4008 A FR (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber - Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.81 g/cc
1.81 g/cc
ASTM D 792
Filler Content 45 %
45 %
Primary Additive
Linear Mold Shrinkage 0.0015 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0015 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 186 MPa
27000 psi
ASTM D 638
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
ASTM D 638
Tensile Modulus 18.6 GPa
2700 ksi
ASTM D 638
Flexural Strength 262 MPa
38000 psi
ASTM D 790
Flexural Modulus 17.2 GPa
2500 ksi
ASTM D 790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.17 mm
2.00 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 6.41 J/cm

@Thickness 3.17 mm
12.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 279 °C
535 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 0.7937 mm
V-0

@Thickness 0.03125 in
Processing Properties Metric English Comments
Melt Temperature 329 - 343 °C
625 - 650 °F
Mold Temperature 65.6 - 163 °C
150 - 325 °F
Drying Temperature 107 °C
225 °F
Dry Time 4 - 6 hour
4 - 6 hour
Moisture Content 0.10 %
0.10 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi