RTP Company RTP 4006 A FR Hot Water Moldable Polyphthalamide (PPA); Glass Fiber Reinforced - Flame Retardant

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 4006 A FR Hot Water Moldable Polyphthalamide (PPA); Glass Fiber Reinforced - Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.69 g/cc
1.69 g/cc
ASTM D 792
Additive Loading 35 %
35 %
Primary Additive
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0040 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 179 MPa
26000 psi
ASTM D 638
Elongation at Break 2.0 %
2.0 %
ASTM D 638
Tensile Modulus 14.5 GPa
2100 ksi
ASTM D 638
Flexural Strength 248 MPa
36000 psi
ASTM D 790
Flexural Modulus 13.8 GPa
2000 ksi
ASTM D 790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.20 mm
2.00 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 6.41 J/cm

@Thickness 3.20 mm
12.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 274 °C
525 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Processing Properties Metric English Comments
Melt Temperature 329 - 343 °C
625 - 650 °F
Mold Temperature 65.6 - 163 °C
150 - 325 °F
Drying Temperature 107 °C

@Time 14400 - 21600 sec
225 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.10 %
0.10 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi