RTP Company RTP 399 X 96257 Polycarbonate (PC), Glass Fiber - PTFE Lubricated - Perfluoropolyether Oil

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass + PTFE Filled
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 399 X 96257 Polycarbonate (PC), Glass Fiber - PTFE Lubricated - Perfluoropolyether Oil.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm

@Thickness 3.17 mm
0.0030 - 0.0050 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 96.5 MPa
14000 psi
ASTM D 638
Elongation at Break 3.0 - 4.0 %
3.0 - 4.0 %
ASTM D 638
Tensile Modulus 6.89 GPa
1000 ksi
ASTM D 638
Flexural Strength 159 MPa
23000 psi
ASTM D 790
Flexural Modulus 6.21 GPa
900 ksi
ASTM D 790
Izod Impact, Notched 1.33 J/cm

@Thickness 3.17 mm
2.50 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 8.01 J/cm

@Thickness 3.17 mm
15.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 138 °C
280 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 132 °C
270 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
ASTM D 257
Surface Resistivity per Square >= 1.00e+14 ohm
>= 1.00e+14 ohm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 82.2 - 121 °C
180 - 250 °F
Drying Temperature 121 °C
250 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi