RTP Company RTP 399 X 129955 E Polycarbonate (PC), Flame Retardant - Transparent

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 399 X 129955 E Polycarbonate (PC), Flame Retardant - Transparent.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Linear Mold Shrinkage 0.00600 - 0.00900 cm/cm

@Thickness 3.20 mm
0.00600 - 0.00900 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.6 MPa
8500 psi
ASTM D 638
Elongation at Break >= 10.0 %
>= 10.0 %
ASTM D 638
Tensile Modulus 2.07 GPa
300 ksi
ASTM D 638
Flexural Strength 93.1 MPa
13500 psi
ASTM D 790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D 790
Izod Impact, Notched 8.01 J/cm

@Thickness 3.20 mm
15.0 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched NB

@Thickness 3.20 mm
NB

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
265 °F
ASTM D 648
Flammability, UL94 V-2

@Thickness 0.200 mm
V-2

@Thickness 0.00787 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Glow Wire Test 850 °C

@Thickness 3.00 mm
1560 °F

@Thickness 0.118 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
Glow Wire Flammability Index; IEC 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 82.2 - 121 °C
180 - 250 °F
Drying Temperature 121 °C

@Time 14400 sec
250 °F

@Time 4.00 hour
Moisture Content 0.0200 %
0.0200 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi