RTP Company RTP 399 X 121668 B Polycarbonate (PC) Flame Retardant - Halogen Free - Wear Alloy - APWA (All Polymeric Wear Additive)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 399 X 121668 B Polycarbonate (PC) Flame Retardant - Halogen Free - Wear Alloy - APWA (All Polymeric Wear Additive).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0060 - 0.010 cm/cm

@Thickness 3.20 mm
0.0060 - 0.010 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.1 MPa
9000 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 2.76 GPa
400 ksi
ASTM D 638
Flexural Strength 103 MPa
15000 psi
ASTM D 790
Flexural Modulus 2.96 GPa
430 ksi
ASTM D 790
Izod Impact, Notched 0.694 J/cm

@Thickness 3.20 mm
1.30 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 6.14 J/cm

@Thickness 3.20 mm
11.5 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 76.7 °C
170 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 249 - 288 °C
480 - 550 °F
Mold Temperature 65.6 - 82.2 °C
150 - 180 °F
Drying Temperature 121 °C

@Time 14400 sec
250 °F

@Time 4.00 hour
Moisture Content 0.020 %
0.020 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi