RTP Company RTP 385 Polycarbonate (PC) Carbon Fiber

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 385 Polycarbonate (PC) Carbon Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D 792
Additive Loading 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.00050 - 0.0010 cm/cm

@Thickness 3.20 mm
0.00050 - 0.0010 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 159 MPa
23000 psi
ASTM D 638
Elongation at Break 1.5 - 2.5 %
1.5 - 2.5 %
ASTM D 638
Tensile Modulus 19.3 GPa
2800 ksi
ASTM D 638
Flexural Strength 241 MPa
35000 psi
ASTM D 790
Flexural Modulus 15.9 GPa
2300 ksi
ASTM D 790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.20 mm
2.00 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 6.94 J/cm

@Thickness 3.20 mm
13.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity <= 10000 ohm-cm
<= 10000 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 82.2 - 121 °C
180 - 250 °F
Drying Temperature 121 °C

@Time 14400 sec
250 °F

@Time 4.00 hour
Moisture Content 0.020 %
0.020 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi