RTP Company RTP 3583 Fluorinated Ethylene Propylene (FEP), Carbon Fiber - Preliminary Data

Category Polymer , Thermoplastic , Fluoropolymer , FEP , Fluorinated Ethylene Propylene (FEP) with Carbon Fiber Filler
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 3583 Fluorinated Ethylene Propylene (FEP), Carbon Fiber - Preliminary Data.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 2.01 g/cc
2.01 g/cc
ASTM D 792
Filler Content 20 %
20 %
Primary Additive
Linear Mold Shrinkage 0.0050 - 0.0090 cm/cm

@Thickness 3.17 mm
0.0050 - 0.0090 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 27.6 MPa
4000 psi
ASTM D 638
Elongation at Break 0.10 - 1.5 %
0.10 - 1.5 %
ASTM D 638
Tensile Modulus 8.27 GPa
1200 ksi
ASTM D 638
Flexural Strength 48.3 MPa
7000 psi
ASTM D 790
Flexural Modulus 6.89 GPa
1000 ksi
ASTM D 790
Izod Impact, Notched 2.14 J/cm

@Thickness 3.17 mm
4.00 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 3.74 J/cm

@Thickness 3.17 mm
7.00 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity <= 10000 ohm-cm
<= 10000 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 343 - 385 °C
650 - 725 °F
Mold Temperature 93.3 °C
200 °F
Drying Temperature 121 °C
250 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 20.7 - 55.2 MPa
3000 - 8000 psi