RTP Company RTP 3400 RC 210 Liquid Crystal Polymer (LCP), Glass Fiber - UL94 V-0  (discontinued **)

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 3400 RC 210 Liquid Crystal Polymer (LCP), Glass Fiber - UL94 V-0  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data for this product has not been recently verified, please contact RTP Company for more information before specifying this grade.
Physical Properties Metric English Comments
Specific Gravity 1.60 g/cc
1.60 g/cc
ASTM D 792
Linear Mold Shrinkage 0.00010 - 0.0010 cm/cm

@Thickness 3.17 mm
0.00010 - 0.0010 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 124 MPa
18000 psi
ASTM D 638
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
ASTM D 638
Tensile Modulus 19.3 GPa
2800 ksi
ASTM D 638
Flexural Strength 155 MPa
22500 psi
ASTM D 790
Flexural Modulus 14.5 GPa
2100 ksi
ASTM D 790
Izod Impact, Notched 0.908 J/cm

@Thickness 3.17 mm
1.70 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 5.87 J/cm

@Thickness 3.17 mm
11.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 288 °C
>= 550 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 0.500 mm
V-0

@Thickness 0.0197 in
Processing Properties Metric English Comments
Melt Temperature 363 - 399 °C
685 - 750 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 149 °C
300 °F
Dry Time 8 hour
8 hour
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 6.89 - 124 MPa
1000 - 18000 psi