- RTP Company RTP 3299 X 120869 A NAT/BLK Ethylene Tetrafluoroethylene (ETFE), Carbon Fiber
RTP Company RTP 3299 X 120869 A NAT/BLK Ethylene Tetrafluoroethylene (ETFE), Carbon Fiber
| Category | Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE |
| Manufacturer | RTP Company |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 3299 X 120869 A NAT/BLK Ethylene Tetrafluoroethylene (ETFE), Carbon Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.72 g/cc | 1.72 g/cc | ASTM D 792 |
| Linear Mold Shrinkage | 0.0013 cm/cm @Thickness 3.17 mm |
0.0013 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.6 MPa | 8500 psi | ASTM D 638 |
| Elongation at Break | 0.50 % | 0.50 % | ASTM D 638 |
| Tensile Modulus | 17.2 GPa | 2500 ksi | ASTM D 638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D 790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 3.17 mm |
2.50 ft-lb/in @Thickness 0.125 in |
D 256 |
| Izod Impact, Unnotched | 2.40 J/cm @Thickness 3.17 mm |
4.50 ft-lb/in @Thickness 0.125 in |
ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 1000 ohm-cm | 10 - 1000 ohm-cm | ASTM D 257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 293 - 343 °C | 560 - 650 °F | |
| Mold Temperature | 65.6 - 149 °C | 150 - 300 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 2 hour | 2 hour | |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Glass Filled 5143 HS Nylon 6/6
- Fiberfil® J-61/20/E Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled
- Thermal Ceramics Saffil® Bulk Fiber
- Loctite® 4205 Thermally Resistant Ethyl Cyanoacrylate Bonding Adhesive
- ChevronTexaco Aries® 220
- DSM Arnite® T08 200 (extrusion) PBT (European and Asian Grade)
- ChevronTexaco TEGRA® ISO 68 Synthetic Compressor Oil
- Fainplast Compounds GA 74/R Flexible PVC, Flame Retardant Sheathing
- Kraiburg TPE THERMOLAST® K TC4CSZ Thermoplastic Elastomer, Optimized compression set (Unverified Data**)&
- DuPont Nucrel® 0903B Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film (discontinued **)
Copyright © lookpolymers.com All Rights Reserved