RTP Company RTP 3102  Perfluoroalkoxy (PFA) Glass Fiber 15%  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PFA , Fluorocarbon PFA with Glass Fiber Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 3102  Perfluoroalkoxy (PFA) Glass Fiber 15%  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass Fiber 15%Comments:Glass FiberUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for this product has not been recently verified, please contact RTP Company for more information before specifying this grade.
Physical Properties Metric English Comments
Specific Gravity 2.20 g/cc
2.20 g/cc
ASTM D792
Filler Content 15 %
15 %
Water Absorption 0.040 %
0.040 %
24 hours at 23°C; ASTM D570
Linear Mold Shrinkage 0.0050 cm/cm

@Thickness 3.17 mm
0.0050 in/in

@Thickness 0.125 in
ASTM D955
0.0080 cm/cm

@Thickness 6.35 mm
0.0080 in/in

@Thickness 0.250 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 41.4 MPa
6000 psi
ASTM D638
Elongation at Break 4.0 - 6.0 %
4.0 - 6.0 %
ASTM D638
Modulus of Elasticity 4.83 GPa
700 ksi
ASTM D638
Flexural Yield Strength 65.5 MPa
9500 psi
ASTM D790
Flexural Modulus 4.14 GPa
600 ksi
ASTM D790
Izod Impact, Notched 3.20 J/cm

@Thickness 3.17 mm
6.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 6.41 J/cm

@Thickness 3.17 mm
12.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 149 °C
300 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Per testing by RTP Company; ASTM D3801
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Processing Temperature 316 - 366 °C
600 - 690 °F
Mold Temperature 149 - 232 °C
300 - 450 °F
Injection Pressure 55.2 - 82.7 MPa
8000 - 12000 psi
Descriptive Properties Value Comments
Color Natural/Black