RTP Company RTP 305 FR L Polycarbonate (PC), Glass Fiber - Flame Retardant - Non-PBBO/E - Lubricated - UL94 V-0

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 305 FR L Polycarbonate (PC), Glass Fiber - Flame Retardant - Non-PBBO/E - Lubricated - UL94 V-0.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The RTP series of flame retardant, glass fiber reinforced polycarbonate materials offer dimensional stability with improved heat distortion and ignition resistance performance over the base resin. RTP 305 FR L includes lubricants for enhanced processing.
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
ASTM D 792
Filler Content 30 %
30 %
Primary Additive
Water Absorption 0.070 %
0.070 %
24 hrs @ 23°C; ASTM D 570
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM D 785
Tensile Strength at Break 124 MPa
18000 psi
ASTM D 638
Elongation at Break 3.0 - 4.0 %
3.0 - 4.0 %
ASTM D 638
Tensile Modulus 8.96 GPa
1300 ksi
ASTM D 638
Flexural Strength 179 MPa
26000 psi
ASTM D 790
Flexural Modulus 7.93 GPa
1150 ksi
ASTM D 790
Izod Impact, Notched 1.60 J/cm

@Thickness 3.17 mm
3.00 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 8.01 J/cm

@Thickness 3.17 mm
15.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 146 °C
295 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
ASTM D 257
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Dielectric Strength 18.1 kV/mm
460 kV/in
Short Term; in oil; ASTM D 149
Dissipation Factor 0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 82.2 - 121 °C
180 - 250 °F
Drying Temperature 121 °C
250 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi