RTP Company RTP 300 TFE 10 Polycarbonate (PC), PTFE Lubricated

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, PTFE Filled
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 300 TFE 10 Polycarbonate (PC), PTFE Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D 792
Linear Mold Shrinkage 0.00500 - 0.0100 cm/cm

@Thickness 3.20 mm
0.00500 - 0.0100 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D 638
Elongation at Break >= 10.0 %
>= 10.0 %
ASTM D 638
Tensile Modulus 2.41 GPa
350 ksi
ASTM D 638
Flexural Strength 79.3 MPa
11500 psi
ASTM D 790
Flexural Modulus 2.28 GPa
330 ksi
ASTM D 790
Izod Impact, Notched 1.87 J/cm

@Thickness 3.20 mm
3.50 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 18.7 J/cm

@Thickness 3.20 mm
35.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
265 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 - 1.00e+16 ohm-cm
1.00e+14 - 1.00e+16 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 288 - 327 °C
550 - 620 °F
Mold Temperature 82.2 - 121 °C
180 - 250 °F
Drying Temperature 121 °C

@Time 14400 sec
250 °F

@Time 4.00 hour
Moisture Content 0.0200 %
0.0200 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi