RTP Company RTP 300 HF L UV Polycarbonate (PC), High Flow - Lubricated - UV Stabilized

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, UV Stabilized
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 300 HF L UV Polycarbonate (PC), High Flow - Lubricated - UV Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0060 - 0.010 cm/cm

@Thickness 3.17 mm
0.0060 - 0.010 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.1 MPa
9000 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 2.07 GPa
300 ksi
ASTM D 638
Flexural Strength 86.2 MPa
12500 psi
ASTM D 790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D 790
Izod Impact, Notched 8.28 J/cm

@Thickness 3.17 mm
15.5 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched NB

@Thickness 3.17 mm
NB

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
260 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 82.2 - 121 °C
180 - 250 °F
Drying Temperature 121 °C
250 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi