RTP Company RTP 300 GB 20 SE A Polycarbonate (PC), Glass Bead - UL94 V-2

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 300 GB 20 SE A Polycarbonate (PC), Glass Bead - UL94 V-2.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D 792
Filler Content 20 %
20 %
Primary Additive
Water Absorption 0.15 %
0.15 %
24 hrs @ 23°C; ASTM D 570
Linear Mold Shrinkage 0.0055 - 0.0075 cm/cm

@Thickness 3.17 mm
0.0055 - 0.0075 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D 785
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D 638
Elongation at Break 6.0 - 9.0 %
6.0 - 9.0 %
ASTM D 638
Tensile Modulus 2.76 GPa
400 ksi
ASTM D 638
Flexural Strength 96.5 MPa
14000 psi
ASTM D 790
Flexural Modulus 2.96 GPa
430 ksi
ASTM D 790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.17 mm
1.20 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 10.7 J/cm

@Thickness 3.17 mm
20.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 138 °C
280 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 132 °C
270 °F
ASTM D 648
Flammability, UL94 V-2

@Thickness 1.59 mm
V-2

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 600 °F
Mold Temperature 82.2 - 121 °C
180 - 250 °F
Drying Temperature 121 °C
250 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi