Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D 792 |
Filler Content | 33 % | 33 % | Primary Additive |
Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0010 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 145 MPa | 21000 psi | ASTM D 638 |
Elongation at Break | 2.0 - 5.0 % | 2.0 - 5.0 % | ASTM D 638 |
Tensile Modulus | 8.96 GPa | 1300 ksi | ASTM D 638 |
Flexural Strength | 221 MPa | 32000 psi | ASTM D 790 |
Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D 790 |
Izod Impact, Notched | 1.98 J/cm @Thickness 3.17 mm |
3.70 ft-lb/in @Thickness 0.125 in |
D 256 |
Izod Impact, Unnotched | 11.7 J/cm @Thickness 3.17 mm |
22.0 ft-lb/in @Thickness 0.125 in |
ASTM D4812 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Melt Temperature | 243 - 279 °C | 470 - 535 °F | |
Mold Temperature | 54.4 - 93.3 °C | 130 - 200 °F | |
Drying Temperature | 82.2 °C | 180 °F | |
Dry Time | 2 hour | 2 hour | |
Moisture Content | 0.20 % | 0.20 % | |
Dew Point | -17.8 °C | 0.000 °F | |
Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi |