RTP Company RTP 299 A X 92682 J Nylon 6 (PA), High Gravity Compound

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 299 A X 92682 J Nylon 6 (PA), High Gravity Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 11.0 g/cc
11.0 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0030 - 0.0080 cm/cm

@Thickness 3.17 mm
0.0030 - 0.0080 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.4 MPa
6000 psi
ASTM D 638
Elongation at Break 0.40 - 0.70 %
0.40 - 0.70 %
ASTM D 638
Tensile Modulus 16.5 GPa
2400 ksi
ASTM D 638
Flexural Strength 58.6 MPa
8500 psi
ASTM D 790
Flexural Modulus 14.5 GPa
2100 ksi
ASTM D 790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm
1.00 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 1.07 J/cm

@Thickness 3.17 mm
2.00 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 243 - 279 °C
470 - 535 °F
Mold Temperature 54.4 - 93.3 °C
130 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 2 hour
2 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi