RTP Company RTP 285 D Nylon 6/12 (PA), Carbon Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Carbon Fiber Filler
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 285 D Nylon 6/12 (PA), Carbon Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D 792
Filler Content 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 207 MPa
30000 psi
ASTM D 638
Elongation at Break 2.0 - 3.0 %
2.0 - 3.0 %
ASTM D 638
Tensile Modulus 19.3 GPa
2800 ksi
ASTM D 638
Flexural Strength 331 MPa
48000 psi
ASTM D 790
Flexural Modulus 17.2 GPa
2500 ksi
ASTM D 790
Izod Impact, Notched 1.12 J/cm

@Thickness 3.17 mm
2.10 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 9.61 J/cm

@Thickness 3.17 mm
18.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 218 °C
425 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity <= 100 ohm-cm
<= 100 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 249 - 285 °C
480 - 545 °F
Mold Temperature 60.0 - 93.3 °C
140 - 200 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 4 hour
4 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi