RTP Company RTP 283 Nylon 6/6 (PA); Carbon Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Carbon Fiber Filled
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 283 Nylon 6/6 (PA); Carbon Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D 792
Additive Loading 20 %
20 %
Primary Additive
Linear Mold Shrinkage 0.00050 - 0.0020 cm/cm

@Thickness 3.20 mm
0.00050 - 0.0020 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
Elongation at Break 2.0 - 3.0 %
2.0 - 3.0 %
ASTM D 638
Tensile Modulus 15.2 GPa
2200 ksi
ASTM D 638
Flexural Strength 296 MPa
43000 psi
ASTM D 790
Flexural Modulus 13.8 GPa
2000 ksi
ASTM D 790
Izod Impact, Notched 0.694 J/cm

@Thickness 3.20 mm
1.30 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 8.54 J/cm

@Thickness 3.20 mm
16.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity <= 1000 ohm-cm
<= 1000 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 277 - 299 °C
530 - 570 °F
Mold Temperature 65.6 - 107 °C
150 - 225 °F
Drying Temperature 79.4 °C

@Time 14400 sec
175 °F

@Time 4.00 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi