RTP Company RTP 2700 S-80A Saturated Styrenic Block Copolymer, General Purpose

Category Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2700 S-80A Saturated Styrenic Block Copolymer, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 0.890 g/cc
0.890 g/cc
ASTM D 792
Linear Mold Shrinkage 0.018 - 0.025 cm/cm

@Thickness 3.20 mm
0.018 - 0.025 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Hardness, Shore A 77
77
10 s delay; ASTM D 2240
Tensile Strength at Break 11.04 MPa
1601 psi
ASTM D 412
Tensile Strength, Yield 2.78 MPa

@Strain 100 %
403 psi

@Strain 100 %
ASTM D 412
Elongation at Break 684 %
684 %
ASTM D 412
Tear Strength 43.6 kN/m
249 pli
Die C; ASTM D 624
Peel Strength 1.75 kN/m
10.0 pli
PP (50% VLF); Failure at interface; 90 degrees, 20 in/min (500 mm/min); ISO 813
3.16 kN/m
18.0 pli
PP (30% VLF); Failure at interface; 90 degrees, 20 in/min (500 mm/min); ISO 813
4.38 kN/m
25.0 pli
PP; Failure at interface; 90 degrees, 20 in/min (500 mm/min); ISO 813
Compression Set 30 %

@Temperature 23.0 °C,
Time 79200 sec
30 %

@Temperature 73.4 °F,
Time 22.0 hour
Method B; Type 2; ASTM D 395
55 %

@Temperature 70.0 °C,
Time 79200 sec
55 %

@Temperature 158 °F,
Time 22.0 hour
Method B; Type 2; ASTM D 395
Processing Properties Metric English Comments
Melt Temperature 177 - 232 °C
350 - 450 °F
Mold Temperature 15.6 - 37.8 °C
60.0 - 100 °F
Drying Temperature 76.7 °C

@Time 7200 sec
170 °F

@Time 2.00 hour
Injection Pressure 34.5 - 68.9 MPa
5000 - 10000 psi