RTP Company RTP 2500 A TFE 10 UV Polycarbonate/ABS Alloy (PC/ABS), PTFE Lubricated - UV Stabilized

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2500 A TFE 10 UV Polycarbonate/ABS Alloy (PC/ABS), PTFE Lubricated - UV Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D 792
Additive Loading 10 %
10 %
Primary Additive
Linear Mold Shrinkage 0.0060 - 0.010 cm/cm

@Thickness 3.17 mm
0.0060 - 0.010 in/in

@Thickness 0.125 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.4 MPa
7750 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 2.41 GPa
350 ksi
ASTM D 638
Flexural Strength 89.6 MPa
13000 psi
ASTM D 790
Flexural Modulus 2.76 GPa
400 ksi
ASTM D 790
Izod Impact, Notched 4.27 J/cm

@Thickness 3.17 mm
8.00 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Izod Impact, Unnotched 18.7 J/cm

@Thickness 3.17 mm
35.0 ft-lb/in

@Thickness 0.125 in
ASTM D 4812
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 243 - 274 °C
470 - 525 °F
Mold Temperature 51.7 - 93.3 °C
125 - 200 °F
Drying Temperature 93.3 °C

@Time 14400 sec
200 °F

@Time 4.00 hour
Moisture Content 0.020 %
0.020 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi