RTP Company RTP 2299 X 80218 Polyetheretherketone (PEEK), PTFE Lubricated
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled |
| Manufacturer | RTP Company |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 2299 X 80218 Polyetheretherketone (PEEK), PTFE Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D 792 |
| Linear Mold Shrinkage | 0.015 - 0.025 cm/cm @Thickness 3.17 mm |
0.015 - 0.025 in/in @Thickness 0.125 in |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D 638 |
| Elongation at Break | 6.0 - 10 % | 6.0 - 10 % | ASTM D 638 |
| Tensile Modulus | 2.07 GPa | 300 ksi | ASTM D 638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D 790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D 256 |
| Izod Impact, Unnotched | 6.94 J/cm @Thickness 3.17 mm |
13.0 ft-lb/in @Thickness 0.125 in |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM E 831 |
| CTE, linear, Transverse to Flow | 76.9 µm/m-°C | 42.7 µin/in-°F | ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D 648 |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 - 1.00e+16 ohm-cm | 1.00e+14 - 1.00e+16 ohm-cm | ASTM D 257 |
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | short term, in oil; ASTM D 149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 349 - 399 °C | 660 - 750 °F | |
| Mold Temperature | 135 - 177 °C | 275 - 350 °F | |
| Drying Temperature | 149 °C @Time 10800 sec |
300 °F @Time 3.00 hour |
|
| Moisture Content | 0.10 % | 0.10 % | |
| Dew Point | -28.9 °C | -20.0 °F | |
| Injection Pressure | 82.7 - 124 MPa | 12000 - 18000 psi |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 49 GF 30 Polypropylene Homopolymer, 30% Glass Fiber
- Plastcom SLOVAMID 66 MI LS PA66, improved strength
- Polymax® Maxelast® P2880 TPE, PP Overmold or Standalone use
- Park Electrochemical Nelco® NH9350 PTFE Laminate, Woven-Glass and Ceramic Reinforced
- Ravago Manufacturing Americas Hylon® N1043HL Nylon 6/6 (DAM)
- SABIC Innovative Plastics Lexan® ML3021A PC (Europe-Africa-Middle East)
- Total HDPE 6280 High Density Polyethylene, Injection Molding Resin
- 3M Scotchlite™ 680CR-14 Removable Reflective Graphic Film with Comply™ Adhesive
- Chang Chun Plastic PBT2100 Fire Retardant PBT
Copyright © lookpolymers.com All Rights Reserved