RTP Company RTP 2282 HF TFE 15 Polyetheretherketone (PEEK), Carbon Fiber Reinforced - PTFE Lubricated

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2282 HF TFE 15 Polyetheretherketone (PEEK), Carbon Fiber Reinforced - PTFE Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D 792
Filler Content 15 %
15 %
Primary Additive
Linear Mold Shrinkage 0.0020 cm/cm

@Thickness 3.17 mm
0.0020 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 179 MPa
26000 psi
ASTM D 638
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
ASTM D 638
Tensile Modulus 14.5 GPa
2100 ksi
ASTM D 638
Flexural Strength 262 MPa
38000 psi
ASTM D 790
Flexural Modulus 13.1 GPa
1900 ksi
ASTM D 790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.17 mm
1.20 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 5.34 J/cm

@Thickness 3.17 mm
10.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 288 °C
550 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity <= 1.00e+6 ohm-cm
<= 1.00e+6 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 349 - 399 °C
660 - 750 °F
Mold Temperature 163 - 218 °C
325 - 425 °F
Drying Temperature 149 °C
300 °F
Dry Time 3 hour
3 hour
Moisture Content 0.10 %
0.10 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 82.7 - 124 MPa
12000 - 18000 psi