RTP Company RTP 2200 LF GB 30 Polyetheretherketone (PEEK), Glass Bead

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2200 LF GB 30 Polyetheretherketone (PEEK), Glass Bead.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D 792
Filler Content 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.0080 - 0.015 cm/cm

@Thickness 3.17 mm
0.0080 - 0.015 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.8 MPa
11000 psi
ASTM D 638
Elongation at Break 6.0 - 10 %
6.0 - 10 %
ASTM D 638
Tensile Modulus 5.52 GPa
800 ksi
ASTM D 638
Flexural Strength 152 MPa
22000 psi
ASTM D 790
Flexural Modulus 5.86 GPa
850 ksi
ASTM D 790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm
1.00 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 4.81 J/cm

@Thickness 3.17 mm
9.00 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 349 - 399 °C
660 - 750 °F
Mold Temperature 163 - 218 °C
325 - 425 °F
Drying Temperature 149 °C
300 °F
Dry Time 3 hour
3 hour
Moisture Content 0.10 %
0.10 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 82.7 - 124 MPa
12000 - 18000 psi