RTP Company RTP 2187 Polyetherimide (PEI); Carbon Fiber

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2187 Polyetherimide (PEI); Carbon Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.43 g/cc
1.43 g/cc
ASTM D 792
Water Absorption 0.18 %

@Time 86400 sec
0.18 %

@Time 24.0 hour
ASTM D 570
Additive Loading 40 %
40 %
Primary Additive
Linear Mold Shrinkage 0.00050 cm/cm

@Thickness 3.20 mm
0.00050 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 241 MPa
35000 psi
ASTM D 638
Elongation at Break 1.3 %
1.3 %
ASTM D 638
Tensile Modulus 30.3 GPa
4400 ksi
ASTM D 638
Flexural Strength 345 MPa
50000 psi
ASTM D 790
Flexural Modulus 26.9 GPa
3900 ksi
ASTM D 790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.20 mm
1.20 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 5.87 J/cm

@Thickness 3.20 mm
11.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity <= 1000 ohm-cm
<= 1000 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 354 - 399 °C
670 - 750 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C

@Time 14400 sec
300 °F

@Time 4.00 hour
Moisture Content 0.040 %
0.040 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 82.7 - 124 MPa
12000 - 18000 psi