RTP Company RTP 2181 HEC HF Polyetherimide (PEI), Nickel-Coated Carbon Fiber - Electrically Conductive - EMI/RFI Shielding - High Flow - Easy Molding

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Nickel Coated Graphite Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2181 HEC HF Polyetherimide (PEI), Nickel-Coated Carbon Fiber - Electrically Conductive - EMI/RFI Shielding - High Flow - Easy Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data for this product has not been recently verified, please contact RTP Company for more information before specifying this grade.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D 792
Additive Loading 10 %
10 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0020 in/in

@Thickness 0.125 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 114 MPa
16500 psi
ASTM D 638
Elongation at Break 2.5 - 4.5 %
2.5 - 4.5 %
ASTM D 638
Tensile Modulus 7.58 GPa
1100 ksi
ASTM D 638
Flexural Strength 207 MPa
30000 psi
ASTM D 790
Flexural Modulus 6.89 GPa
1000 ksi
ASTM D 790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.17 mm
1.20 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Izod Impact, Unnotched 4.27 J/cm

@Thickness 3.17 mm
8.00 ft-lb/in

@Thickness 0.125 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
5VA

@Thickness 3.17 mm
5VA

@Thickness 0.125 in
Electrical Properties Metric English Comments
Volume Resistivity <= 100 ohm-cm
<= 100 ohm-cm
ASTM D 257
Surface Resistance <= 1e+05
<= 1e+05
ESD STM11.11
Surface Resistivity per Square <= 1.00e+6 ohm
<= 1.00e+6 ohm
ASTM D 257
Static Decay <= 0.50 sec
<= 0.50 sec
FTMS101C; 4046.1
Processing Properties Metric English Comments
Melt Temperature 366 - 399 °C
690 - 750 °F
Mold Temperature 141 - 177 °C
285 - 350 °F
Drying Temperature 149 °C

@Time 14400 sec
300 °F

@Time 4.00 hour
Moisture Content 0.040 %
0.040 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 82.7 - 124 MPa
12000 - 18000 psi