Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 20% Glass Fiber |
Manufacturer | |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | RTP Company RTP 2103 Z Polyetherimide (PEI) Glass Fiber 20% - FDA Type
(discontinued **)&l.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
Filler Content | 20 % | 20 % | |
Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 145 MPa | 21000 psi | ASTM D638 |
Elongation at Break | 3.35 % | 3.35 % | ASTM D638 |
Modulus of Elasticity | 6.89 GPa | 1000 ksi | ASTM D638 |
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
Izod Impact, Unnotched | 5.50 J/cm @Thickness 3.17 mm |
10.3 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Processing Temperature | 349 - 382 °C | 660 - 720 °F | |
Mold Temperature | 135 - 177 °C | 275 - 350 °F | |
Injection Pressure | 82.7 - 124 MPa | 12000 - 18000 psi |
Descriptive Properties | Value | Comments |
---|---|---|
Color | Natural/Black |